CO content 6% Tungsten Carbide Rod Blanks fixed length, with Density 14.8 g / cm3
Description:
Tungsten carbide rod HF06 (K10), a WC-Co alloy, Co content 6%, made up by 0.4μm ultra fine grain carbide powder with superior performance and homogeneous compact structure is produced by Hot Isolation Pressing sintering technique, though which cemented carbide material is fully consolidated by simultaneous application of heat and pressure, leading to a product that contains little or no porosity. Therefore, product quality is stable and reliable, and has long service life.
Our carbide rods are sintered by vacuum HIP furnace so that we can guarantee products are with good densification and high transverse rupture strength.
Our solid carbide bars can be offered in various sizes. Apart from abundant standard specification in stock, we also accept custom order.
Production process: dosing, wet-milling, pressing, sintering, quality test, finished product, packaging.
- ISO Range: K10
- with 94% tungsten carbide, 6% cobalt
- Made of 0.4 micron ultrafine TC powder
- Hardness: 93.5-93.8 HRA
- Bending strength: >3200 MPa
- Density: 14.8 g/cm3
- As sintered
- Standard inch length: unground fixed length
Specifications:
Solid rods- cut to length(inch):
| D | L | D | L | ||||||||
| (inch) | (mm) | (inch) | Tol (+1.5 mm) | (inch) | (mm) | (inch) | Tol (+1.5 mm) | ||||
| 3/16 | 0.188 | 4.763 | 1 1/2 |  Sell